Q:Causes of Common Production Problems in Q235 Spiral Pipes

Common Defects and Causes of Spiral Steel Pipes: Loosening, bubbles, shrinkage cavities, residues, non-metallic inclusions, segregation, white spots, cracks, and various abnormal fracture defects in spiral steel pipes.

Causes of Segregation in Q235 Spiral Pipes: During casting and solidification, selective crystallization and diffusion can cause the aggregation of certain elements, leading to uneven chemical composition. Depending on the distribution location, this can be classified as ingot segregation, center segregation, and point segregation.

Causes of porosity in Q235 spiral tubes: During hot working, gaps are created by the solidification shrinkage of low-melting-point materials and the release of gas, preventing the steel from being welded. Based on their basic distribution, porosity can be divided into two types: centrally located type and generally loose type.